Particle characteristics’ influence on FLASH sintering of potassium sodium niobate: A relationship with conduction mechanisms

Ricardo Serrazina, Camila Ribeiro, Maria E. V. Costa, Luis Pereira, Paula M. Vilarinho, Ana M. O. R. Senos

Research output: Contribution to journalArticlepeer-review

2 Citations (Scopus)

Abstract

The considerable decrease in temperature and time makes FLASH sintering a more sustainable alternative for materials processing. FLASH also becomes relevant if volatile elements are part of the material to be processed, as in alkali‐based piezoelectrics like the promising lead‐free K0.5Na0.5NbO3 (KNN). Due to the volatile nature of K and Na, KNN is difficult to process by conventional sintering. Although some studies have been undertaken, much remains to be understood to properly engineer the FLASH sintering process of KNN. In this work, the effect of FLASH temperature, TF, is studied as a function of the particle size and impurity content of KNN powders. Differences are demonstrated: while the particle size and impurity degree markedly influence TF, they do not significantly affect the densification and grain growth processes. The conductivity of KNN FLASH‐sintered ceramics and KNN single crystals (SCs) is compared to elucidate the role of particles’ surface conduction. When particles’ surfaces are not present, as in the case of SCs, the FLASH process requires higher temperatures and conductivity values. These results have implications in understanding FLASH sintering towards a more sustainable processing of lead‐free piezoelectrics.

Original languageEnglish
Article number1321
JournalMaterials
Volume14
Issue number5
DOIs
Publication statusPublished - 9 Mar 2021

Keywords

  • Ceramics
  • Conduction mechanisms
  • FLASH sintering
  • FLASH temperature
  • Impurities
  • KNaNbO
  • KNN
  • Particle size
  • Single crystals

Fingerprint

Dive into the research topics of 'Particle characteristics’ influence on FLASH sintering of potassium sodium niobate: A relationship with conduction mechanisms'. Together they form a unique fingerprint.

Cite this